Prepainted Hot Dip Galvanized Steel Coil

Galvanized steel is a hot-dipped coated metal that provides customers with better resistance to corrosive environments. To create galvanized steel, cold rolled steel is submerged into a molten zinc bath, known as the hot-dip process (galvanization can also be achieved through continuous galvanizing). When the material is removed from the zinc bath and cooled a reaction to the oxygen in the air occurs. The reaction causes the zinc coating to become part of the steel creating the well-recognized spangled finish.

Galvanized coil: a thin steel sheet that immerses the steel sheet into the molten zinc bath to make its surface adhere with a layer of zinc. It is mainly produced by continuous galvanizing process, that is, the rolled steel plate is continuously immersed in the zinc melting bath to make galvanized steel plate; Alloyed galvanized steel sheet. This kind of steel plate is also made by hot dip method, but it is heated to about 500 ℃ immediately after coming out of the groove to form an alloy coating of zinc and iron. The galvanized coil has good coating adhesion and weldability.

Galvanized steel is a hot-dipped coated metal that provides customers with better resistance to corrosive environments. To create galvanized steel, cold rolled steel is submerged into a molten zinc bath, known as the hot-dip process (galvanization can also be achieved through continuous galvanizing). When the material is removed from the zinc bath and cooled a reaction to the oxygen in the air occurs. The reaction causes the zinc coating to become part of the steel creating the well-recognized spangled finish.

Galvanized coil: a thin steel sheet that immerses the steel sheet into the molten zinc bath to make its surface adhere with a layer of zinc. It is mainly produced by continuous galvanizing process, that is, the rolled steel plate is continuously immersed in the zinc melting bath to make galvanized steel plate; Alloyed galvanized steel sheet. This kind of steel plate is also made by hot dip method, but it is heated to about 500 ℃ immediately after coming out of the groove to form an alloy coating of zinc and iron. The galvanized coil has good coating adhesion and weldability.

Galvanized Steel coil: a thin steel sheet that immerses the steel sheet into the molten zinc bath to make its surface adhere with a layer of zinc. It is mainly produced by continuous galvanizing process, that is, the rolled steel plate is continuously immersed in the zinc melting bath to make galvanized steel plate; Alloyed galvanized steel sheet. This kind of steel plate is also made by hot dip method, but it is heated to about 500 ℃ immediately after coming out of the groove to form an alloy coating of zinc and iron. The galvanized coil has good coating adhesion and weldability.

Galvanized coil: a thin steel sheet that immerses the steel sheet into the molten zinc bath to make its surface adhere with a layer of zinc. It is mainly produced by continuous galvanizing process, that is, the rolled steel plate is continuously immersed in the zinc melting bath to make galvanized steel plate; Alloyed galvanized steel sheet. This kind of steel plate is also made by hot dip method, but it is heated to about 500 ℃ immediately after coming out of the groove to form an alloy coating of zinc and iron. The galvanized coil has good coating adhesion and weldability.

Galvanized steel is a hot-dipped coated metal that provides customers with better resistance to corrosive environments. To create galvanized steel, cold rolled steel is submerged into a molten zinc bath, known as the hot-dip process (galvanization can also be achieved through continuous galvanizing). When the material is removed from the zinc bath and cooled a reaction to the oxygen in the air occurs. The reaction causes the zinc coating to become part of the steel creating the well-recognized spangled finish.

Galvanized steel is a hot-dipped coated metal that provides customers with better resistance to corrosive environments. To create galvanized steel, cold rolled steel is submerged into a molten zinc bath, known as the hot-dip process (galvanization can also be achieved through continuous galvanizing). When the material is removed from the zinc bath and cooled a reaction to the oxygen in the air occurs. The reaction causes the zinc coating to become part of the steel creating the well-recognized spangled finish.